The high temperature strength of the joint increased with the increasing of brazing temperature.

且在试验温度范围内,接头强度随钎焊温度升高呈上升趋势.

Brazing temperature and lasting hours have certain influences to wearing and tearing ratio.

钎焊温度和时间对磨耗比有一定的影响。

As the brazing temperature increased, shear strength of the joints increased and then decreased.

在本研究的范围内，随着钎焊温度的升高，接头剪切强度表现为先升高后降低的趋势。

When the brazing temperature exceeded 650 ℃, the tensile strength decreased.

温度高于650℃，抗拉强度降低；

Study on effect of brazing temperature on wear properties of brazed WC coatings

钎焊温度对WC金属布钎焊耐磨层性能研究

Electron beam brazing temperature field PID control system

电子束钎焊温度场PID控制系统

The influence of brazing temperature and time on the wettability is significant.

钎焊温度和时间对润湿性有重要影响。

However, the brazing temperature had little influence on the liquefying time.

而钎焊温度对中间层的液化时间没有明显的影响。

Study of Temperature Close-cycle Control System in Glow Discharge Brazing Process

辉光放电钎焊温度控制系统的研究

QJ301 is a copper-based brazing welding used solvent, the solvent particles uniformly fine at a temperature of850-1150 ℃, copper and brass brazing alloys gas welding or brazing flux when used.

QJ301是一种基于铜焊接用的铜焊溶剂，本溶剂颗粒均匀细微，在温度为850-1150℃，钎焊紫铜及黄铜合金气焊或钎焊时作助熔剂用。

X ray image analysis of high temperature brazing seam for corrugated plate sandwich structure

波纹板夹层结构高温钎焊焊缝X射线影像分析

Numerical Simulation and Analysis of the Temperature Field for Direct Current GTAW Arc Brazing

直流GTAW电弧钎焊温度场的数值模拟及分析

Study of the Action Mechanism of cobalt in Copper-based High Temperature Brazing Alloy

铜基高温钎料中钴作用机制的研究

R& D of Low Temperature Ceramic/ Metal Brazing Alloy

环保型陶瓷/金属低温钎料的研究与开发

Design of temperature control system of high frequency induction brazing diamond tool

高频感应钎焊金刚石工具温控系统设计

The theoretical rules among the high temperature performance of the brazing alloy, strain rate and the function of Co alterant are analyzed.

分析了钎料高温性能与应变速率、钴的变质剂作用等因素之间的理论规律。

The temperature of the joint should be hot enough to melt the brazing alloy.

连接部位的温度应该高到能够融化铜焊合金.

The furnace is applicable for high temperature degassing and vacuum brazing.

并能广泛适用于高温脱气、真空钎焊等场合.

The Al-Cu eutectic brazing metal is made to braze pure aluminium substrate in vacuum. The diffusion phenomenon of Cu in pure aluminum bar under different brazing temperature and heat preservation time is investigated by means of SEM and EDS.

制备Al-Cu共晶合金钎料，用SEM和EDS研究不同钎焊温度和保温时间条件下，纯铝棒料基体对接真空钎焊接头Cu元素的扩散行为。